CHEMICAL COMPONET:
ADMISSUS (wt%) | C | Mn | Si | Cr | Ni | Mo | P | S | Fe | Nb+Ti |
EXEMPLUM PENSI HABEO | 0.01 | 0.12 | 0.44 | 21.7 | 62.7 | 8.25 | 0.003 | 0.003 | 0.9 | 3.41 |
MACHINA proprietas:
POSSESSIO | VICTORITAS (MPa) | PROLATIO VIS (MPa) | IMAPACT VALEO J/℃ | PROLATIO(%) | ||||
EXEMPLUM PENSI HABEO | - | 765 | - | 38 |
Praecipua compositio est 61Ni-22Cr-9Mo-3.5Nb+Ta, quae frequentissima est materia nickel-chromium-molybdaenorum glutino.
Cum glutino sui tutela TIG filum glutino est, tunica protectiva in occipitium stagni firmae penetrabit, ac densum stratum tegumentum uniformiter in anteriori et posteriori loco pugillo formant, ita ut transitus utriusque partis firmae sint. non oxidized.Unius glutino utrinque formatur, et scoria glutino sponte excidet postquam pugillus locus refrigeratur.
Modus fili glutino eadem prorsus est ac vulgaris nickel innixa arcus glutini argonis.Peculiaris superficies tunica nullum effectum habet adversam in proprietates nuptiarum et mechanicarum.Arcus est stabilis, formatio pulchra, et fluxus metalli calidus est bonus.
-
Shaanxi Pucheng -50℃ propane sphaericae cisternina project
-
2.3 decies cados SBM Fast4ward FPSO
-
Shandong nuclei potentia CV20
CHEMICAL COMPONET:
ADMISSUS (wt%) | C | Mn | Si | Cr | Ni | Mo | P | S | Fe | Nb+Ti |
EXEMPLUM PENSI HABEO | 0.01 | 0.12 | 0.44 | 21.7 | 62.7 | 8.25 | 0.003 | 0.003 | 0.9 | 3.41 |
MACHINA proprietas:
POSSESSIO | VICTORITAS (MPa) | PROLATIO VIS (MPa) | IMAPACT VALEO J/℃ | PROLATIO(%) | ||||
EXEMPLUM PENSI HABEO | - | 765 | - | 38 |