Nickel alloys TIG ERNiCr-3 supellectilem solidandi accessiones
CHEMICAL COMPONET:
| ADMISSUS (wt%) | C | Mn | Si | Cr | Ni | Mo | Fe | Nb+Ta | P | S |
| GB/T REGULAE | 0.10 | 2.5-3.5 | 0.50 | 18.0-22.0 | ≥67.0 | - | 3.0 | 2.0-3.0 | - | - |
| AWS Rules | 0.10 | 2.5-3.5 | 0.50 | 18.0-22.0 | ≥67.0 | - | 3.0 | 2.0-3.0 | 0.03 | 0.014 |
| EXEMPLUM PENSI HABEO | 0.024 | 2.78 | 0.05 | 20.69 | 72.85 | 0.15 | 0.67 | 2.44 | 0.001 | 0.001 |
MACHINA proprietas:
| POSSESSIO | VICTORITAS (MPa) | PROLATIO VIS (MPa) | IMAPACT VALEO J/℃ | PROLATIO(%) | ||||
| GB/T REGULAE | - | - | - | - | ||||
| AWS Rules | - | - | - | - | ||||
| EXEMPLUM PENSI HABEO | - | 710 | 170-196 | 39 | ||||
Nickel-chromium-ferrum nickel-base offensionis gasi glutini filum, compositio nominalis est 72%Ni-20%Cr-3%Mn-2.5%Nb+Ta.
Metallum fusum bonas proprietates mechanicas habet, bonum corrosio resistentia, oxidatio alta resistentia et vires subrepentes.
Arcus stabilis, formosus formans, bonus fluxus ferri fusilis, processu egregio glutino effectus.
-
Qinghai Youjian Wunan Oilfield
-
Welding materiae ad LNG vehiculum utres
-
Princeps pressura calefacientis Hangzhou Boiler Group Co
CHEMICAL COMPONET:
| ADMISSUS (wt%) | C | Mn | Si | Cr | Ni | Mo | Fe | Nb+Ta | P | S |
| GB/T REGULAE | 0.10 | 2.5-3.5 | 0.50 | 18.0-22.0 | ≥67.0 | - | 3.0 | 2.0-3.0 | - | - |
| AWS Rules | 0.10 | 2.5-3.5 | 0.50 | 18.0-22.0 | ≥67.0 | - | 3.0 | 2.0-3.0 | 0.03 | 0.014 |
| EXEMPLUM PENSI HABEO | 0.024 | 2.78 | 0.05 | 20.69 | 72.85 | 0.15 | 0.67 | 2.44 | 0.001 | 0.001 |
MACHINA proprietas:
| POSSESSIO | VICTORITAS (MPa) | PROLATIO VIS (MPa) | IMAPACT VALEO J/℃ | PROLATIO(%) | ||||
| GB/T REGULAE | - | - | - | - | ||||
| AWS Rules | - | - | - | - | ||||
| EXEMPLUM PENSI HABEO | - | 710 | 170-196 | 39 | ||||