I. Overview
Celeri progressione machinariae industriae productionis, structurae iunctae sicut hodierni vasa machinalis et pressionis in dies magis magisque ad trends leves ac leves augentur.Requisita pro ferro vires gradus altiores et altiores sunt, non solum bona quaerunt proprietates mechanicas comprehensivae, sed etiam processus boni, weldability et rima resistentia.
Q690 ferro ad summum iuncta est compage ferrum, ubi Q stat pro cede, et 690 significat cedere viribus aequis 690MPa.690MPa gradus ferreus habet altam cede et distrahentes vires, et late in fodienda machinis carbonis, machinae constructionis, machinae marinae, tabulae suboles, pressiones vasorum, etc., ferrum requirunt habere altitudinem cedere vires et lassitudinem limitem, bonam ictum, duritiem, frigus. formabilitas et optimae coniugii.
2.Brief introductio Q690 laminae ferro
| International Q690 gradus ferro | Q690A | Q690B | Q690C | Q690D | Q690E | Q690F |
| Pluma | calidum advolvit | restinguere + temperare ( restincto et temperato ) . | ||||
| immunditia content | Superiore P/S | humilis P / S * | Minimum P/S | |||
| Inpulsa Requisita | NO | Normalis temperatus inpulsa | 0℃ | -20℃ | -40℃ | -60℃ |
Tamen nunc 690MPa lamina ferrea pro vasis pressuris domesticis maxime fundatur in vexillum Europae EN10028-6, et proprietates pertinentes in tabula sequenti breviter recensentur:
| Cede 690MPA ferro ad Europae vexillum pressionis apparatu | P690Q | P690QH | P69QL1 | P69QL2 |
| Pluma | grano subtili exstincto et ferro temperato | |||
| viribus opus | Yield≥690MPa(platea thickness≤50mm) Tensile770-940MPa | |||
| immunditia content | P≤0.025%, S≤0.015% | P≤0.03%, S≤0.010% | ||
| Inpulsa Requisita | 20℃≥60J | 20℃≥60J | 0℃≥60J | -20℃≥40J |
| 0℃≥40J | 0℃≥40J | -20℃≥40J | -40℃≥27J | |
| -20℃≥27J | -20℃≥27J | -40℃≥27J | -60℃≥27J | |
| Pelagus application areas | Pressura-portantes structuras vel pressura vasa humilis impulsum durities servata | Sphaerica tristique magna technica | Liquefactum gas marinae liquor piscinae | |
Sicut ferrum laminam pro repono lacus et pressione facultatem, debet habere bonam vim et duritiem, frigus inflexio perficiendi et humilis rima sentiendi.Etsi chalybs extincta et temperata Q690 inferiorem carbonis aequipollentem et excellentem proprietates comprehensivas habet, tamen durities quamdam inclinationem habet comparatam cum aliis 50/60kg pressionis vasis chalybis, et curatio caloris post iuncta requiritur.Sed numerus studiorum experimentalium ostenditur quod pro ferro glutino consumables Q690, frigiditas incussus temperaturae durities signanter debilitabitur post accentus levationem caloris curationis, et cum augmento caloris curationis temperatus et diminutio ictum temperatus, depravatio. glutino consumabilis durities manifestior erit.Ideo magnae practicae significatio est ut summus fortitudo, summus impetus durities, et calor tractabiles virgas glutinosas ad Q690 ferrum ad bene applicandum Q690 ferrum ad pressionis instrumenta portantem, ferrum materias reducere, et gratuita fabricanda reducere.
3.Brief introductio nostrae Q690 virgae ferro glutino
| Item | Standard | Genus cutis | Verticitas | marisque |
| GEL-118M | AWS A5.5 E1108MISO 18275-BE7618-N4M2A | Ferrum pulveris humilis hydrogenii genus | DC+/AC | Maximum robur, humilis hydrogenii, alta depositio efficientiae, stabilia mechanica propria, excellentia humilis temperatura impacta durities in -50°C, et bonum ictum durities in -40°C post caloris curatio |
| GEL-758 | AWS A5.5 E11018-GISO 18275-BE7618-G A | Ferrum pulveris humilis hydrogenii genus | DC+/AC | Consectetuer ultra-humilis, alta depositio efficientiae, alta durities (-60℃≥70J), bonum ictum durities in -40/-50℃ post curatio caloris |
| GEL-756 | AWS A5.5 E11016-GISO 18275-BE7616-G A | Humilis hydrogenii kalium type | AC/DC+ | Consectetuer ultra-low, AC/DC+ dual-propositum, altum impulsum durities (-60℃≥70J), bonum ictum durities in -50/-60℃ post curationem caloris |
4.Q690 ferrum glutino mechanica perficientur ostentationem
| Item | Ut iuncta mechanica proprietatibus | ||||||
| cede MPA | Distrahens MPA | Praetende % | Impulsum proprietas J/ | Radiographica test | Diffusible hydrogenii Ml/100g | ||
| -50℃ | -60℃ | ||||||
| AWS A5.5 E11018M | 680- 760 | ≥760 | ≥20 | ≥27 | - | I | - |
| ISO 18275-B E7618-N4M2A | 680- 760 | ≥760 | ≥18 | ≥27 | - | I | - |
| GEL-118M | 750 | 830 | 21.5 | 67 | 53 | I | 3.2 |
| AWS A5.5 E1101X-G | ≥670 | ≥760 | ≥15 | - | - | I | - |
| ISO 18275B E761X-GA | ≥670 | ≥760 | ≥13 | - | - | I | - |
| GEL-758 | 751 | 817 | 19.0 | 90 | 77 | I | 3.4 |
| GEL-756 | 764 | 822 | 19.0 | 95 | 85 | I | 3.6 |
Illustrare:
1. "X" in fonte rubro notatum in Latin et American Standard Europae genus medicamenti pellis repraesentat.
2. GEL-758 correspondet E11018-G, ISO 18275-B E7618-G A in signis respective AWS, ISO.
3. GEL-756 correspondet E11016-G, ISO 18275-B E7616-G A in signis respective AWS, ISO.
Mechanica proprietatum Q690 ferrum glutino in calore curationis status
| Item | Mechanica caloris agitur status | ||||||
| cede MPA | Distrahens MPA | Praetende % | Impulsum proprietas J/ | Calefactio * h | |||
| -40℃ | -50℃ | -60℃ | |||||
| Project propositum | ≥670 | ≥760 | ≥15 | ≥60 | ≥52 | ≥47 | 570*2 |
| GEL-118M | 751 | 827 | 22.0 | 85 | 57 | - | 570*2 |
| GEL-758 | 741 | 839 | 20.0 | 82 | 66 | 43 | 570*2 |
| GEL-756 | 743 | 811 | 21.5 | 91 | 84 | 75 | 570*2 |
Illustrare:
1. AWS et ISO signa mutata non habent caloris curatio necessaria ad praedicta producta.Curae superiores caloris perstringuntur ex condicionibus technicis plerisque clientibus ac solum referendi sunt.
2. GEL-118M post caloris curationi -40°C impulsum excellentem habet duritiem, et impulsum depravationis in -50°C manifestius est.
3. Post caloris curationem, GEL-758 duritiem in -40°C praestantem habet impulsum, bonam duritiem in -50°C impulsum, et manifestam corruptionem ad frigiditatem in -60°C.
4. Humilis temperatura ictum durities deteriorationis GEL-756 post curatio caloris est relative parva, et humilis temperatura durities in -60°C adhuc bona est.
Weldability demonstratio Q690 virgae ferro glutino
1.Flat vitta glutino (φ4.0mm)
GEL-118M vitta plana glutino ante et post recrementum remotionis (DC+)
Ante et post GEL-758 vitta plana glutino remotionis scoria (DC+)
GEL-756 ante et post recrementum remotionis vitta plana glutino (AC)
GEL-756 vitta plana glutino ante et post recrementum remotionis (DC+))
Q690 cautes ferro glutino cudo
1. Repono glutino consumables;
Consummabiles glutino commendantur ut sub perpetua temperie et siccis conditionibus condiantur, et in cursulis vel cautes ponantur, evitando directum contactum cum muris et terra.
2. Praeparatio ante glutino:
Prorsus humorem, aeruginem, maculas olei, etc. in superficie materiae basin, neve humorem superficiem, vel expositionem pluviis et nivis.
3. Windproof mensurae;
Cum glutino cautum est, ut maximus ventus celeritatem in loco glutino 2m/s non excedat.Alioquin praesidia facienda sunt.
4. Preheating:
Commendatur ut instrumento electrico calefactionis ad calefactionem operis ad supra 150°C ante glutino calefacto.Priusquam glutino assedas, prehendi debet supra 150°C.
5. Iacuit temperatura et via imperium:
Per totum processum glutino, temperatura interpassi non debet esse minor quam preheating temperies, et commendatum temperatura transeuntis 150-220°C est.
6. Hydrogenium remotionis post glutino;
Post pugillo commissura iuncta, statim temperatura electrici calefactionis ad 250 ~ 300 auget, calefactum retinent per 2 ad 4 horas, et tardius refrigerant.
Si opusculi crassitudo sit ≥50mm, tempus tenendi extendi debet ad 4-6 horas, ac deinde tardius refrigeratur.
Sub conditionibus magnae crassitudinis et magnae cohibitionis, plus siccitatis adici potest post glutino ad crassitudinem 1/2, et tardius ad temperiem interpassi refrixisse.
7. Tabulatum layout:
Commendatur ut multi-strati et multi-passionis glutino utantur, et celeritas glutino assidua celeritate retineatur.