I. Overview
Cum celeri progressione chemicae et industriae internationalis logistics, ferro intemerato obterere et receptacula reposita, late utuntur in translatione et repositione chemicae, cibi et potus, energiae et aliarum materiarum.Ob eximiam eius humilitatem temperationis duritiem et repugnantiam bonam corrosionis, austeniticum chalybem immaculatum late adhibetur in constructione piscinarum repositionis cryogenicae, instrumentorum et magnarum structurarum cryogenicarum.
Cryogenic repono tank
2. Brevis introductio nostri -196℃ humilis temperatus impacto incorrupto ferro glutino consumables
Categoria | Nomen | Model | Standard | Animadverte | |
GB/YB | AWS | ||||
Electrode | GES-308LT | A002 | E308L-16 | E308L-16 | -196℃≥31J |
Fluxum filum | GFS-308LT | - | TS 308L-F C11 | E308LT1-1 | -196℃≥34J |
Solidum filum | GTS-308LT (TIG) | - | H022Cr21Ni10 | ER308L | -196℃≥34J |
GMS-308LT (MIG) | - | H022Cr21Ni10 | ER308L | -196℃≥34J | |
SAW | GWS-308/ GXS-300 | - | S F308L FB-S308L | ER308L | -196℃≥34J |
3.Our electrode GES-308LT (E308L-16)
Ad mercatum postulandum, societas nostra varias temperaturas ultra-humilis evolvit, alta durities austenitica electrodes chalybis immaculata, compositio chemicae metalli depositi (ut in Tabula 1) et proprietatibus mechanicis stabilis (ut in Tabula ostensum est) 2), et praecellens habet processum omnium positionis glutino euismod, et excellentia humilitatis temperaturae ictum duritiem, impulsum sui ferrite quantitatis in ictum valorem (Tabula III).
1.Chemical compositio deposita metallica
E308L-16 | C | Mn | Si | P | S | Ni | Cr | Mo | Cu | N | Fn |
NB (%) | 0.04 | 0.5-2.5 | 1.0 | 0.030 | 0.018 | 9.0-12.0 | 18.0-21.0 | 0.75 | 0.75 | - | - |
Sample1 | 0.022 | 1.57 | 0.62 | 0.014 | 0.006 | 10.25 | 19.23 | 0.018 | 0.027 | 0.041 | 6.5 |
Sample2 | 0.093 | 2.15 | 0.46 | 0.018 | 0.005 | 10.44 | 19.19 | 0.013 | 0.024 | 0.45 | 3.8 |
Sample3 | 0.093 | 1.37 | 0.49 | 0.017 | 0.007 | 11.79 | 18.66 | 0.031 | 0.027 | 0.041 | 0.6 |
Table 1
2.Mechanical proprietatibus depositum metallum
E308L-16 | Cede MPa | Tensile MPa | Prolongatio % | -196℃imparct J/℃ | GB/T4334-2020 E corrosio intergranulare | Radiographic inspectionem | Animadverte | |
Unius pretii | Mediocris valorem | |||||||
NB | - | 510 | 30 | - | - | - | I | - |
Sample1 | 451 | 576 | 42 | 32/32/33 | 32.3 | quid | I | - |
Sample2 | 436 | 563 | 44 | 39/41/39 | 39.7 | quid | I | - |
Sample3 | 412 | 529 | 44.5 | 52/53/55 | 53.3 | quid | I | - |
Table 2
3. effectus moles metallum ferrite deposita in impulsum
4.Display processus glutino (φ3.2mm)
Rectum glutino ante et post recrementum remotionem (DC +)
Pipeline glutino ante et post recrementum remotionem (DC +)
4. Cautio pro vertical welding
1. Minimum current glutino utendum;
2. Arcum quam maxime humilem custodi;
3. Cum arcus avertit ad utramque partem rimam, paulisper subsiste, et oscillatio latitudinis intra tria tempora diametri electrodis contineatur.
5.Pipeline picturam applicationem glutino consumables
Pro -196℃ humilis-temperatus impulsum chalybem incorruptam glutino consumables, post annos investigationis et evolutionis consumabilium glutino, iam habemus correspondentem sustentationem glutino consumabilium ad virgas glutinosas, coros solidos, nucleos fluxos et arcus immersos, et manu electronico continuum arcum elaborasse. glutino consumables pro omni positione glutino, et multas res gestas machinativas habet, grata clientibus ad consulendum et eligendum!