CHEMICAL COMPONET:
ADMISSUS (wt%) | C | Mn | Si | Cr | Ni | Mo | P | S | Cu |
GB/T REGULAE | 0.12 | 0.80-1.50 | 0.30-0.90 | 1.00-1.60 | - | 0.40-0.65 | 0.03 | 0.03 | 0.40 |
AWS Rules | - | - | - | - | - | - | - | - | - |
EXEMPLUM PENSI HABEO | 0.105 | 1.00 | 0.60 | 1.25 | 0.03 | 0.5 | 0.01 | 0.005 | 0.05 |
MACHINA proprietas:
POSSESSIO | VICTORITAS (MPa) | PROLATIO VIS (MPa) | IMAPACT VALEO J/℃ | PROLATIO(%) | Caloris curatio Cxh | |||||
GB/T REGULAE | 470 | 550 | - | 17 | 690*1 | |||||
AWS Rules | 470 | 550 | - | 15 | 690*1 | |||||
EXEMPLUM PENSI HABEO | 489 | 609 | 109/0 | 26 | 690*1 |
PARAMETERS WELDING RECOMMENDED:
DIAMETERS SPECIFICATIONS(mm) | 1.0 | 1.2 | 1.6 | |||||||
ELECTRICITY (Amp) | H/W | 50-220 | 80-350 | 170-550 | ||||||
O/W* | 50-120 | 80-150 | - |
Gas scutum welding filum pro 550MPa classis calor ferro resistens.
Filum leve pascens, arcus stabilis, pulchra formans, bonum fluxus ferri fusilis, technologiae glutino optimae.
Metallum fusum bonas proprietates mechanicas habet, altum Mn contentum, bonam raritatem resistendi et pactionem formans.
-
Mei Jin Hua Sheng ethylene glycol synthetica turris
-
Welding materiae ad plenas blasphemiae
-
PX1212 H suggestum supplere navis
CHEMICAL COMPONET:
ADMISSUS (wt%) | C | Mn | Si | Cr | Ni | Mo | P | S | Cu |
GB/T REGULAE | 0.12 | 0.80-1.50 | 0.30-0.90 | 1.00-1.60 | - | 0.40-0.65 | 0.03 | 0.03 | 0.40 |
AWS Rules | - | - | - | - | - | - | - | - | - |
EXEMPLUM PENSI HABEO | 0.105 | 1.00 | 0.60 | 1.25 | 0.03 | 0.5 | 0.01 | 0.005 | 0.05 |
MACHINA proprietas:
POSSESSIO | VICTORITAS (MPa) | PROLATIO VIS (MPa) | IMAPACT VALEO J/℃ | PROLATIO(%) | Caloris curatio Cxh | |||||
GB/T REGULAE | 470 | 550 | - | 17 | 690*1 | |||||
AWS Rules | 470 | 550 | - | 15 | 690*1 | |||||
EXEMPLUM PENSI HABEO | 489 | 609 | 109/0 | 26 | 690*1 |
PARAMETERS WELDING RECOMMENDED:
DIAMETERS SPECIFICATIONS(mm) | 1.0 | 1.2 | 1.6 | |||||||
ELECTRICITY (Amp) | H/W | 50-220 | 80-350 | 170-550 | ||||||
O/W* | 50-120 | 80-150 | - |