Low-Alloy Steels Manual Electrode E8016-C4 Mod Jack-up aggeribus Consumables
Praecipua pars 1.5%Ni est, humilis hydrogenii potassii genus manu electrode, in -50C temperatura operante, ictum spissitudo metalli depositi optimum est.
Arcus stabilis, fundendi minus, corona bona, remotio scoria facilis
X-Ray effectus est optimus.
CHEMICAL COMPONET:
ADMISSUS (wt%) | C | Si | Mn | P | S | Ni | Cr | Mo | Other | |
GB/T REGULAE | 0.093 | 0.42 | 1.07 | 0.009 | 0.007 | 1.49 | 0.025 | 0.005 | - |
MACHINA proprietas:
POSSESSIO | VICTORITAS (MPa) | PROLATIO VIS (MPa) | Prolongatio(%) | IMAPACT VALEO J/℃ | Caloris curatio ° C * h * | |||||
GB/T REGULAE | 505 | 600 | 23 | 105/-50 | 620*1 |
PARAMETERS WELDING RECOMMENDED:
DIAMETERS SPECIFICATIONS(mm) | 2.6*350 | 3.2*350 | 4.0*400 | 5.0*400 | |||||
ELECTRICITY (Amp) | H/W | 70-100 | 100-140 | 140-180 | 180-230 | ||||
O/W* | 60-90 | 90-130 | 120-160 | - |
Sanmen Power nuclei
-
JU2000E jack-sursum diam diam
Harbin electrici tres portae CMT
CHEMICAL COMPONET:
ADMISSUS (wt%) | C | Si | Mn | P | S | Ni | Cr | Mo | Other | |
GB/T REGULAE | 0.093 | 0.42 | 1.07 | 0.009 | 0.007 | 1.49 | 0.025 | 0.005 | - |
MACHINA proprietas:
POSSESSIO | VICTORITAS (MPa) | PROLATIO VIS (MPa) | Prolongatio(%) | IMAPACT VALEO J/℃ | Caloris curatio ° C * h * | |||||
GB/T REGULAE | 505 | 600 | 23 | 105/-50 | 620*1 |
PARAMETERS WELDING RECOMMENDED:
DIAMETERS SPECIFICATIONS(mm) | 2.6*350 | 3.2*350 | 4.0*400 | 5.0*400 | |||||
ELECTRICITY (Amp) | H/W | 70-100 | 100-140 | 140-180 | 180-230 | ||||
O/W* | 60-90 | 90-130 | 120-160 | - |